Hastelloy G-30 Grade N06030 Nickel Chromium Alloy Plate Sheet

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Model NO.: Hastelloy G-30
• Type: Nickel Plate
• Stock: Stock Available
• Third Part Inspection: Available
• Sample: Free
• Trade Terms: EXW, Fob, CIF, CFR
• Surface: Mirror, Brushed, Mill Finished, Polished etc.
• Transport Package: Standard Export Package
• Specification: As Customer′s Request
• Trademark: Mingson
• Origin: China
• HS Code: 7506200000
• Production Capacity: 7000 Tons Per Year

Product Description

1.Product Name: Nickel Alloy Plate/Sheet
2.Grade: Hastelloy G-30(UNS N06030)
3.Thickness: 0.6mm-70mm, Length: ≤12000mm, Wide:≤2500mm

4.Features: N06030 is a high chromium nickel-base alloy which has superior corrosion resistance over most other nickel and iron-base alloys in commercial phosphoric acid as well as many complex environments containing highly oxidizing acids such as nitric/hydrochloric, nitric/hydrofluoric and sulfuric acids. It resists the formation of grain boundary precipitates in the heat-affected zone, making it suitable for use in most chemical process environments in the as-welded condition.
5.Applications: Chemical processing involving phosphoric acid, sulfuric acid and nitric acid; nuclear fuel reprocessing; nuclear waste processing; pickling operations; petrochemical; fertilizer manufacture; pesticide manufacture; and gold ore extraction.
6.Physical Properties

Density	Melting Range	Electrical Resistivity	Dilatation Coefficient	Heat Conductivity	Thermal Diffusivity	Specific Heat Capacity
g/cm3	°C	1.28	11.5×10E^-6	14	3.6×10E^-6	398
8.23	1335-1380

7.The Minimum Mechanical Properties At Normal Temperature

Alloy and State	Tensile Strength	Yield Strength	Rate of Elongation	Elasticity Modulus
Annealing	Rm N/mm^2	RP0.2N/mm^2	A5%	212
	>586	>241	>30

8.Chemical Composition

%	Ni	Cr	Mo	Fe	W	Co	C	Mn	Si	P	S	Cu	Nb
MIN	Balance	28	4	13	1.5	-	-	0.3	0.2	-	-	1	0.3
MAX		31.5	6	17	4	5	0.03	1.5	0.8	0.04	0.02	2.4	1.5