Alloy C-22 is a versatile Ni-Cr-Mo-W alloy with better comprehensive corrosion resistance performance than other Ni-Cr-Mo alloys, including Alloy C-276, Alloy C-4 and Alloy 625. Alloy C-22 has outstanding resistance to pitting, crevice corrosion and stress corrosion cracking. It has excellent resistance to oxidizing aqueous media including wet chlorine and mixtures containing nitric acid or oxidizing acids with chloride ions. It also offers optimum resistance to environments where reducing and oxidizing conditions are encountered in process streams. So it can be used where "upset" conditions are likely to occur or in multi-purpose plants. Alloy C-22 has exceptional resistance to a wide variety of chemical process environments, including strong oxidizers such as ferric and cupric chlorides, chlorine, hot contaminated solutions (organic and inorganic), formic and acetic acids, acetic anhydride, and seawater and brine solutions. It resists the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as-welded condition.
CHEMICAL COMPOSITION
| % |
Ni |
Cr |
Mo |
Fe |
W |
Co |
C |
Mn |
Si |
P |
S |
V |
| MIN |
Balance |
20 |
12.5 |
2 |
2.5 |
- |
- |
- |
- |
- |
- |
|
| MAX |
22.5 |
14.5 |
6 |
3.5 |
2.5 |
0.015 |
0.5 |
0.08 |
0.02 |
0.35 |
0.02 |
PHYSICAL PROPERTIES
| Density |
Melting Range |
Tensile Strength |
Yield Strength |
Rate of Elongation |
| g/cm3 |
°C |
Rm N/mm2 |
RP0.2N/mm2 |
A5% |
| 8.94 |
1325-1370 |
≥690 |
≥310 |
≥40% |